（时间：3小时满分：100分）
| 题 号 | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 |
| 满 分 | 4 | 12 | 20 | 9 | 8 | 9 | 12 | 18 | 8 |
| H 1.008 | 相对原子质量 | He 4.003 | |||||||||||||||
| Li 6.941 | Be 9.012 | B 10.81 | C 12.01 | N 14.01 | O 16.00 | F 19.00 | Ne 20.18 | ||||||||||
| Na 22.99 | Mg 24.31 | Al 26.98 | Si 28.09 | P 30.97 | S 32.07 | Cl 35.45 | Ar 39.95 | ||||||||||
| K 39.10 | Ca 40.08 | Sc 44.96 | Ti 47.88 | V 50.94 | Cr 52.00 | Mn 54.94 | Fe 55.85 | Co 58.93 | Ni 58.69 | Cu 63.55 | Zn 63.39 | Ga 69.72 | Ge 72.61 | As 74.92 | Se 78.96 | Br 79.90 | Kr 83.80 |
| Rb 85.47 | Sr 87.62 | Y 88.91 | Zr 91.22 | Nb 92.91 | Mo 95.94 | Tc [98] | Ru 101.1 | Rh 102.9 | Pd 106.4 | Ag 107.9 | Cd 112.4 | In 114.8 | Sn 118.7 | Sb 121.8 | Te 127.6 | I 126.9 | Xe 131.3 |
| Cs 132.9 | Ba 137.3 | La-Lu | Hf 178.5 | Ta 180.9 | W 183.8 | Re 186.2 | Os 190.2 | Ir 192.2 | Pt 195.1 | Au 197.0 | Hg 200.6 | Tl 204.4 | Pb 207.2 | Bi 209.0 | Po [210] | At [210] | Rn [222] |
| Fr [223] | Ra [226] | Ac-La | |||||||||||||||
一．（4分）黄绿色ClO2具有漂白、消毒作用，沸点9.90℃，制备ClO2的方法是：将湿润的KClO3和草酸（固体）混合加热到60℃即得。
1．ClO2的分子构型为 ；
2．制备反应方程式为
3．用此法制备获得的ClO2和其它生成物分离的方法是
二．（12分）传统合成冰晶石（Na3AlF6）的方法是使用萤石（CaF2）为原料，萤石作为一种重要的战略物资需要加以保护，使用磷肥副产氟硅酸钠（Na2SiF6）为原料的方法成为一条合理利用资源、提高经济效益的新方法。冰晶石的生产合成主要由晶种生成、氨解、偏铝酸钠的制备和冰晶石合成四个工段组成。工艺流程如下图所示：
使用这种方法可以得到大量副产品白炭黑。为了提高副产品白炭黑的质量，可以采用外加晶种法，得到的白炭黑用于丁苯橡胶中，拉伸强度可以达到21Mpa，而外加晶种法对冰晶石质量也有影响。
1．冰晶石的化学名称为 ，主要用途是 。
2．副产品白碳黑的化学成分是 ，丁苯橡胶的结构简式是
3．氨解反应方程式是
4．偏铝酸钠的制备反应是
5．冰晶石合成反应方程式是
6．晶种制备的原料为硫酸或氢氟酸、水玻璃、水。分别使用HF和H2SO4合成晶种，生成的冰晶石检验结果如下：
制备晶种用酸对冰晶石质量的影响
| 酸 | F/% | Al% | Na/% | Na︰Al | SiO2 | Fe2O3 | SO42－ |
| HF | 53.00 | 13.26 | 31.00 | 2.74 | 0.564 | 0.010 | 0.11 |
| H2SO4 | 52.58 | 12.68 | 31.82 | 2.95 | 0.247 | 0.006 | 1.49 |
从实验结果看，使用 制晶种，合成的冰晶石质量较好，简述你的理由。
三．（20分）能源是当今社会发展的三大支柱之一，是制约国家经济发展的瓶颈。目前，我国的能源结构主要是煤，还有石油、天然气、核能等，这些能源都是一次不可再生且污染环境的能源，研究和开发清洁而又用之不竭的能源是未来发展的首要任务。科学家预测“氢能”将是未来21世纪最理想的新能源。氢能是利用氢气的燃烧反应放热提供能量，即H